Korean Journal of Materials Research ISSN:1225-0562(Print) 2287-7258(Online) 한국재료학회지

Al-Cr-Si ternary quench ribbons are fabricated using a single roll method and investigated for their structural and thermal properties. In particular, the sinterability is examined by pulse current sintering to obtain the following results. The Al₇₄Cr₂₀Si₆ composition becomes a quasicrystalline single phase; by reducing the amount of Cr, it becomes a twophase mixed structure of Al phase and quasicrystalline phase. As a result of sintering of Al₇₄Cr₂₀Si₆, Al₇₇Cr₁₃Si₁₀ and Al₉₀Cr₆Si₄ compositions, the sintering density is increased with the large amount of Al phase; the sintering density is the highest in Al₉₀Cr₆Si₄ composition. In addition, as a result of investigating the effects of sintering temperature and pressurization on the sintered density of Al₉₀Cr₆Si₄, a sintered compact of 99% or more at 513 K and 500 MPa is produced. In particular, since the Al-Cr-Si ternary crystal is more thermally stable than the Al-Cr binary quaternary crystal, it is possible to increase the sintering temperature by about 100 K. Therefore, using an alloy of Al₉₀Cr₆Si₄ composition, a sintered compact having a sintered density of 99 % or more at 613 K and 250 MPa can be manufactured. It is possible to increase the sintering temperature by using the alloy system as a ternary system. As a result, it is possible to produce a sintered body with higher density than that possible using the binary system, and at half the pressure compared with the conventional Al-Cr binary system.