Effect of Y2O3 Additive Amount on Densification of Reaction Bonded Silicon Carbides Prepared by Si Melt Infiltration into All Carbon Preform

완전 탄소 프리폼으로부터 Si 용융 침투에 의해 제조한 반응 소결 탄화규소의 치밀화에 미치는 Y2O3 첨가량의 영향

Kyeong-Sik Cho1†
,
Min-Ho Jang12
조 경식1†
,
장 민호12
1Department of Advanced Materials Science & Engineering, Kumoh National Institute of Technology, 61, Daehak-ro, Gumi, Gyungbuk 39177, Republic of Korea
2Orange E& C, 140-20, Cheomdangieop 5-ro, Gumi, Gyungbuk 39171, Republic of Korea
1금오공과대학교
2(주)오렌지이앤씨
†Corresponding author E-Mail : kscho@kumoh.ac.kr (K.-S. Cho, KIT)
May 2021. pp. 301-311
PDF XML Citation
Abstract

The conversion of all carbon preforms to dense SiC by liquid infiltration can become a low-cost and reliable method to form SiC-Si composites of complex shape and high density. Reactive sintered silicon carbide (RBSC) is prepared by covering Si powder on top of 0.5-5.0 wt% Y2O3-added carbon preforms at 1,450 and 1,500°C for 2 hours; samples are analyzed to determine densification. Reactive sintering from the Y2O3-free carbon preform causes Si to be pushed to one side and cracking defects occur. However, when prepared from the Y2O3-added carbon preform, an SiC-Si composite in which Si is homogeneously distributed in the SiC matrix without cracking can be produced. Using the Si + C = SiC reaction, 3C and 6H of SiC, crystalline Si, and Y2O3 phases are detected by XRD analysis without the appearance of graphite. As the content of Y2O3 in the carbon preform increases, the prepared RBSC accelerates the SiC conversion reaction, increasing the density and decreasing the pores, resulting in densification. The dense RBSC obtained by reaction sintering at 1,500 °C for 2 hours from a carbon preform with 2.0 wt% Y2O3 added has 0.20% apparent porosity and 96.9% relative density.

Keywords
reaction-bonded silicon carbide
carbon preform
liquid infiltration
relative density
References
1.
K. Tsuno, H. Irikado, K. Hamada, O. Kazuhiko, J. Ishida, S. Suyama, Y. Itoh, N. Ebizuka, H. Eto and Y. Dai, in International Conference on Space Optics-ICSO 2004, ed. J. Costeraste and E. Armandillo, 105681F, Toulouse, France, March-April (2004).
2.
Y. Zhang, J. Zhang, J. Han, X. He and W. Yao, Mater. Lett., 58, 1204 (2004). 10.1016/j.matlet.2003.09.010
3.
K. Tsuno, H. Irikado, K. Oono, S. Suyama and Y. Itoh, in Proc. 6th Inter. Conf. on Space Optics, ESASP-621, Noordwijk, Netherlands, June (2006).
4.
L. E. Matson, M. Y. Chen and B. deBlonk, 2008 Advances Maui Optical and Space Surveillance Technologies Conference, Maui, HI, September (2008).
5.
M. Kotani, Y. Muta, A. Yoshimura, S. Ogihara, T. Imai, H. Katayama, Y. Yui, Y. Tange, K. Enya, H. Kaneda and T. Nakagawa, J. Mater. Eng. Perform., 23, 850 (2014). 10.1007/s11665-013-0827-1
6.
Y.-H. Baik, J. Korean Ceram. Soc., 25, 609 (1988).
7.
Y.-J. Kim, Y.-S. Park, Y.-W. Jung, J.-B. Song, S.-Y. Park and H.-J. Im, J. Korean Soc. Composite Mater., 25, 172 (2012). 10.7234/kscm.2012.25.6.172
8.
I.-S. Han, J.-H. Yang and D.-S. Suhr, J. Korean Ceram. Soc., 30, 69 (1993).
9.
K.-S. Seo, S.-W. Park, J.-W. Ha and Y.-J. Chung, J. Korean Ceram. Soc., 35, 626 (1998).
10.
K. S. Seo, S. W Park and H. S. Song, J. Korean Ceram. Soc., 36, 655 (1999).
11.
G.-S. Cho, G.-M. Kim and S.-W. Park, J. Korean Ceram. Soc., 46, 534 (2009). 10.4191/KCERS.2009.46.5.534
12.
C.-S. Kwon, Y.-S. Oh, S.-M. Lee, Y. Han, H.-I. Shina, Y. Kim and S. Kim, J. Korean Powder Metall. Inst., 21, 467 (2014). 10.4150/KPMI.2014.21.6.467
13.
B. L. Wing, F. Esmonde-White and J. W. Halloran, J. Am. Ceram. Soc., 99, 3705 (2016). 10.1111/jace.14398
14.
N.-L. Zhang, J.-F. Yang, Y.-C. Deng, B. Wang and P. Yin, Ceram. Int., 45, 15715 (2019). 10.1016/j.ceramint.2019.04.224
15.
S. Songa, B. Lua, Z. Gaob, C. Baoc and Y. Ma, Ceram. Int., 45, 17987 (2019). 10.1016/j.ceramint.2019.06.017
16.
H. Xia, J. Wang, H. Jin, Z. Shi and G. Qiao, Mater. Sci. and Eng., A, 525, 283 (2010). 10.1016/j.msea.2010.08.088
17.
J. C. Margiotta, D. Zhang, D. C. Nagle and C. E. Feeser, J. Mater. Res., 23, 1237 (2008). 10.1557/JMR.2008.0167
18.
A. S. Mukasyan, Y.-C. Lin, A. S. Rogachev and D. O. Moskovskikh, J. Am. Ceram. Soc., 96, 111 (2013). 10.1111/jace.12107
19.
Y. Wang, S. Tan and D. Jiang, Ceram. Int., 30, 435 (2004). 10.1016/S0272-8842(03)00128-7
20.
Y. X. Wang, S. H. Tan and D. L. Jiang, Carbon, 42, 1833 (2004). 10.1016/j.carbon.2004.03.018
21.
A. K. Kercher and D. C. Nagle, Carbon, 41, 3 (2003). 10.1016/S0008-6223(02)00262-2
22.
C. Zollfrank and H. Sieber, J. Am. Ceram. Soc., 88, 51 (2005). 10.1111/j.1551-2916.2004.00028.x
23.
P. Sangsuwan, J. A. Orejas, J. E. Gatica, S. N. Tewari and M. Singh, Ind. Eng. Chem. Res., 40, 5191 (2001). 10.1021/ie001029e
24.
A. Favre, H. Fuzellier and J. Suptil, Ceram. Int., 29, 235 (2003). 10.1016/S0272-8842(02)00110-4
25.
K. Yaqnaba, M. Akasaka, M. Takeuchi, M. Watanabe, T. Narushima and Y. Iguchi, Mater. Trans., JIM, 38, 990 (1997). 10.2320/matertrans1989.38.990
26.
P. Sangsuwan, S. N. Tewari, J. E. Gatica, M. Singh and R. Dickerson, Metall. Mater. Trans. B, 30B, 933 (1999). 10.1007/s11663-999-0099-1
27.
O. Dezellus, F. Hodaj and N. Eustathopoulos, Acta Mater., 50, 4741 (2002). 10.1016/S1359-6454(02)00309-9
28.
H. T. Fang, J. H. Jeon, J. C. Zhu and Z. D. Yin, Carbon, 40, 2559 (2002). 10.1016/S0008-6223(02)00171-9
29.
Y. Song, S. Dhar, L. C. Feldman, G. Chung and J. R. Williams, J. Appl. Phys., 95, 4953 (2004). 10.1063/1.1690097
30.
B. Harder, N. Jacobson and D. Myers, J. Am. Ceram. Soc., 96, 606 (2013). 10.1111/jace.12104
31.
N. S. Jacobson, J. Am. Ceram. Soc., 76, 3 (1993). 10.1111/j.1151-2916.1993.tb03684.x
32.
J. Roy, S. Chandra, S. Das and S. Maitra, Rev. Adv. Mater. Sci., 38, 29 (2014).
33.
S. Ding, S. Zhu, Y. Zeng and D. Jiang, Ceram. Int., 32, 461 (2006). 10.1016/j.ceramint.2005.03.024
34.
A. Maity, D. Kalita, N. Kayal, T. Goswami, O. Chakrabarty and P. G. Rao, Ceram. Int., 38, 4701 (2012). 10.1016/j.ceramint.2012.02.054
35.
K. Biswas, G. Rixecker and F. Aldinger, Mater. Sci. Eng., A, 374, 56 (2004). 10.1016/j.msea.2003.11.037
36.
L. Wu, W. Sun, Y. Chen, Y. Lu, Y. Jiang and Z. Huang, J. Am. Ceram. Soc., 94, 4453 (2011). 10.1111/j.1551-2916.2011.04709.x
37.
A. Noviyanto and D.-H. Yoon, Current Appl. Phys., 13, 287 (2013). 10.1016/j.cap.2012.07.027
38.
H.-M. Oh and H.-K. Lee, Ceram. Int. 46, 12517 (2020).
39.
X. Zhu, Y. Zhou, K. Hirao and Z. Lences, J. Am. Ceram. Soc., 89, 3331 (2006). 10.1111/j.1551-2916.2006.01195.x
40.
X. Zhou, D. Liu, H. Bu, L. Deng, H. Liu, P. Yuan, P. Du and H. Song, Solid Earth Sci., 3, 16 (2018). 10.1016/j.sesci.2017.12.002
41.
Y. Tong, S. Bai, X. Liang, Q. H. Qin and J. Zhai, Ceram. Int., 42, 17174 (2016). 10.1016/j.ceramint.2016.08.007
42.
R. Voytovych, V. Bougiouri, N. R. Calderon, J. Narciso and N. Eustathopoulos, Acta Mater., 56, 2237 (2008). 10.1016/j.actamat.2008.01.011
43.
V. Bougiouri, R. Voytovych, N. Rojo-Calderon, J. Narciso, N. Eustathopoulos, Scr. Mater., 54, 1875 (2006). 10.1016/j.scriptamat.2006.02.015
44.
M. Naikadea, B. Fankhanelc, L. Weberb, A. Ortonad, M. Stelterc and T. Graulea, J. Eur. Ceram. Soc., 39, 735 (2019). 10.1016/j.jeurceramsoc.2018.11.049
45.
A. Casado, J. M. Torralba and S. Milenkovic, Metals, 9, 300 (2019). 10.3390/met9030300
Information
  • Publisher :Materials Research Society of Korea
  • Publisher(Ko) :한국재료학회
  • Journal Title :Korean Journal of Materials Research
  • Journal Title(Ko) :한국재료학회지
  • Volume : 31
  • No :5
  • Pages :301-311
  • Received Date : 2021-02-15
  • Revised Date : 2021-04-24
  • Accepted Date : 2021-05-10
  • DOI :https://doi.org/10.3740/MRSK.2021.31.5.301
Journal Informaiton Korean Journal of Materials Research Korean Journal of Materials Research
Online Submission
  • scopus
  • NRF
  • KOFST
  • crossref crossmark
  • crossref cited-by
  • crosscheck
  • open access
  • ccl
Journal Informaiton Journal Informaiton - close