Characteristics of Basalt Materials Derived from Recycling Steel Industry Slags

Woo-Gwang Jung; Gu-Seul Back; Mi-Jung Yoon; Jee-Wook Lee

doi:10.3740/MRSK.2017.27.5.281

All Issue

2017 Vol.27, Issue 5 Preview Page Next Page

Characteristics of Basalt Materials Derived from Recycling Steel Industry Slags 철강산업 슬래그를 이용하여 제조한 바잘트 소재의 특성

May 2017. pp. 281-288

PDF XML

Abstract

In this study, Fe-Ni slag, converter slag and dephosphorization slag generated from the steel industry, and fly ash or bottom ash from a power plant, were mixed at an appropriate mixing ratio and melted in a melting furnace in a massproduction process for glass ceramics. Then, glass-ceramic products, having a basalt composition with SiO₂, Al₂O₃, CaO, MgO, and Fe₂O₃ components, were fabricated through casting and heat treatment process. Comparison was made of the samples before and after the modification of the process conditions. Glass-ceramic samples before and after the process modification were similar in chemical composition, but Al₂O₃ and Na₂O contents were slightly higher in the samples before the modification. Before and after the process modification, it was confirmed that the sample had a melting temperature below 1250 °C, and that pyroxene and diopside are the primary phases of the product. The crystallization temperature in the sample after modification was found to be higher than that in the sample before modification. The activation energy for crystallization was evaluated and found to be 467 kJ/mol for the sample before the process modification, and 337 kJ/mol for the sample after the process modification. The degree of crystallinity was evaluated and found to be 82% before the process change and 87% after the process change. Mechanical properties such as compressive strength and bending strength were evaluated and found to be excellent for the sample after process modification. In conclusion, the samples after the process modification were evaluated and found to have superior characteristics compared to those before the modification.

Keywords

basalt

slag recycling

Kissinger method

crystallinity

mechanical strength.

References

P. E Tsakiridis, G. D Papadimitriou, S Tsivilis and C Koroneos, J. Hazard. Mater, 152; 805 (2008)

10.1016/j.jhazmat.2007.07.09317869414

S. W Choi, V Kim, W. S Chang and E. Y Kim, J. Concrete, 19; 28 (2007)

K Freidin and E Erell, Cement Concrete Comp, 17; 289 (1995)

10.1016/0958-9465(95)00017-7

M Heikal, I Aiad and I. M Helmy, Cement Concrete Res, 32; 1805 (2002)

10.1016/S0008-8846(02)00867-0

S Kourounis, S Tsivilis, P. E Tsakiridis, G. D Papadimitriou and Z Tsibouki, Cement Concrete Res, 37; 815 (2007)

10.1016/j.cemconres.2007.03.008

P. J Nel and A Tauber, J. South African Inst. Mining Metall; 366 (1970-July)

M. L Oveco lu, J. Euro. Ceram. Soc, 18; 161 (1998)

A. A Francis, J. Am. Ceram. Soc, 88; 1859 (2005)

M. V Folgueras, P. N de Oliveira and O. E Alarcon, Am. Ceram. Soc. Bull; 9201 (2005-Nov)

A. A Francis, Mater. Res. Bull, 41; 1146 (2006)

Z Wang, W Ni, Y Jia, L Zhu and X Huang, J. Non-Crys. Solids, 356; 1554 (2010)

G. A Khater, Ceram. Int, 37; 2193 (2011)

K Zhang, J Liu, W Liu and J Yang, Chemosphere, 85; 689 (2011)

F He, Y Fang, J Xie and J Xie, Mater. Des, 42; 198 (2012)

Y Wang, Q Jiang, G Luo, W Yu and Y Ban, J. Metall, 954021 (2012)

Z Yang, Q Lin, J Xia, Y He, G Liao and Y Ke, J. Alloys Compd, 574; 354 (2013)

Z Yang, Q Lin, S Lu, Y He, G Liao and Y Ke, Ceram. Int, 40; 7297 (2014)

A Kamusheva, E. M. A Hamzawy and A Karamanov, J. Chem. Tech. Metall, 50; 512 (2015)

E Mohamed, P Shahsavari, B Eftekhari-Yekta and V. K Marghussian, Trans. Ind. Ceram. Soc, 74; 1 (2015)

S.-H Chang and H.-J Jung, J. Korean Ceram. Soc, 17(20), (in Korean) (1980)

S.-H Chang and H.-J Jung, J. Korean Ceram. Soc, 17(27), in Korean (1980)

G.-S Back, H. S Park, S. M Seo and W.-G Jung, Met. Mater. Int, 21; 1061 (2015)

G.-S Back, M.-J Yoon and W.-G Jung, Met. Mater. Int, (in press) (2017)

M Rezvani, B Eftekhari-Yekta, M Solati-Hashjin and V. K Marghussian, Ceram. Int, 31; 75 (2005)

S. M Wang, Environ. Sci. Technol, 44; 4816 (2010)

X Ren, W Zhang, Y Zhang, P Zhang and J Liu, Trans. Nonferrous Met. Soc. China, 25; 137 (2015)

ASTM D1857/D1857M, DIN 51730:1998

H. J Jung, Ph.D. Thesis, Controlled Crystallization and Properties of Glasses in the System CaO-MgO-Al₂O₃-SiO₂, United Kingdom. Leed University. (1976)

D. U Tulyaganov, XIX Proceeding of the International Congress on Glass, 198 , Vol. 2 Extended Abstract, Edinburgh, Scotland, 1-6 July (2001)

I. L Denry and J. A Holloway, J. Biomed. Mat. Res, 63; 48 (2002)

H. E Kissinger, J. Res. Natl. Bur. Stand, 57; 217, (US) (1956)

M Ma, W Ni, Y Wang, X Li, F Liu and Z Wang, J. Chin. Ceram. Soc, 37; 609 (2009)

M Rezvani, B Eftekhari-Yekta, M Solati-Hashjin and V. K Marghussian, Ceram. Int, 31; 75 (2005)

J. E Field, J. Appl. Phys, 12; 23, (http://dx.doi. org/10.1063/1.1712848) (1941)

10.1063/1.1712848

S. M Ohlberg and D. W Strickler, J. Am. Ceram. Soc, 45; 170 (1962)

Information

Publisher :Materials Research Society of Korea
Publisher(Ko) :한국재료학회
Journal Title :Korean Journal of Materials Research
Journal Title(Ko) :한국재료학회지
Volume : 27
No :5
Pages :281-288
Received Date : 2017-03-08
Revised Date : 2017-03-30
Accepted Date : 2017-03-31
DOI :https://doi.org/10.3740/MRSK.2017.27.5.281

Korean Journal of Materials Research ISSN:1225-0562(Print) 2287-7258(Online) 한국재료학회지

All Issue